Title: Comparative Study on Several Anti-Corrosion Materials for Power FGD System (几种防腐材料用于电力烟气脱硫系统的比较研究)

In the study organic-inorganic hybrid composite, epoxy modified silicone coating and vinyl ester flake mas-tic were comparatively used as several anti-corrosion materials that provided protection for flue gas desulfu-rization (FGD). The relationship between curing conversion rate of hybrid polymer and temperature was in-vestigated by differential scanning calorimeter (DSC). The adhesion strength, coefficient of thermal expan-sion and flame retardant properties of three anti-corrosion materials were measured and analyzed. A corro-sion test in 8% H2SO4 and 5% HCl at temperature cycle of 40˚C ~ 160˚C was applied to study corrosion re-sistance of several anti-corrosion materials. Gravimetric measurement and morphological observation of three materials before and after corrosion test were comparatively analyzed in the paper. The small weight change and good morphological structure of hybrid composite during corrosion test demonstrate that hybrid composite has better anti-corrosion properties than epoxy modified silicone coating and vinyl ester flake mastic.

Click Here For Complete Article Text

 

   Person Information
   Application Sequencing
Company  Product  Process  Other  Subjects  Event  Event  Date  Location  Publication  Publication  Date Text  Descriptor
  • Coating

  • Lining

  • Corrosion

 

  • Corrosion

 

 

 

 

 

  • Article